Translaminar fracture toughness of interply hybrid laminates under tensile and compressive loads

​
orcId Ortega Novillo, Adrián​ researcherId Ortega Novillo, Adrián​ ​ ​
Ortega Novillo, Adrián
orcId Maimí Vert, Pere​ researcherId Maimí Vert, Pere​ scopusId Maimí Vert, Pere​ ​
Maimí Vert, Pere
orcId González Juan, Emilio Vicente​ researcherId González Juan, Emilio Vicente​ scopusId González Juan, Emilio Vicente​ ​
González Juan, Emilio Vicente
​ ​ ​ ​
Sainz de Aja, J.R.
​ ​ ​ ​
Escalera, F.M de la
​ ​ ​ ​
Cruz, P.
Texto Completo
TranslaminarFracture.pdf embargoed access ​
Solicita copia
Solicita copia
Al rellenar este formulario estáis solicitando una copia del artículo, depositado en el repositorio institucional (DUGiDocs), a su autor o al autor principal del artículo. Será el mismo autor quien decidirá enviar una copia del documento a quien lo solicite si lo considera oportuno. En todo caso, la Biblioteca de la UdG no interviene en este proceso ya que no está autorizada a facilitar artículos cuando éstos son de acceso restringido.
​
Compartir
​
This paper presents an experimental study of the translaminar fracture toughness under tensile and compressive loads of interply hybrid polymer-matrix composite laminates. The studied laminates were obtained by combining two of three different reinforcements: woven carbon fabric, woven glass fabric and unidirectional carbon tape, manufactured using the Resin Transfer Molding (RTM) process. The resulting in-plane quasi-isotropic laminates were generated by changing each material location along the thickness ​
​Tots els drets reservats
Mostrar el registro completo del ítem

Ítems relacionados

Mostrando ítems relacionados por título, autor o materia

Assessment of mode I fatigue delamination of composites through a rapid testing method

Multiple crack initiation in cross-ply laminates under spectrum loadings

Obj. de conferencia open access ​

​

Lay-up effects on the fatigue life of open-hole multidirectional composite laminate specimens subjected to cyclic shear loading