Thermal behavior of several Fe-Ni alloys prepared by mechanical alloying and rapid solidification

​
​ ​ ​ ​
González Gasch, Àlex
orcId Suñol Martínez, Joan Josep​ researcherId Suñol Martínez, Joan Josep​ scopusId Suñol Martínez, Joan Josep​ ​
Suñol Martínez, Joan Josep
orcId Bonastre i Muñoz, Jordi​ ​ ​ ​
Bonastre i Muñoz, Jordi
orcId Escoda i Acero, Ma. Lluïsa​ ​ scopusId Escoda i Acero, Ma. Lluïsa​ ​
Escoda i Acero, Ma. Lluïsa
​ ​ ​ ​
Caleya, J.
Full Text
Thermal-behavior.pdf embargoed access ​
Request a copy
Request a copy
When filling the form you are requesting a copy of the article, that is deposited in the institutional repository (DUGiDocs), at the autor or main autor of the article. It will be the same author who decides to give a copy of the document to the person who requests it, if it considers it appropriate. In any case, the UdG Library doesn’t take part in this process because it is not authorized to provide restricted articles.
​
Share
​
Several Fe-Ni-P-Si alloys were produced in an amorphous state by mechanical alloying and rapid solidification. Thermal behavior of the as prepared alloys was analyzed and compared with identical alloys stored during 1 and 2 years. During annealing time, several exothermic processes related to the structural relaxation were detected at low temperature and with further crystallization at high temperature. As increasing the storage time, the powdered samples were relaxed at lower temperatures. The activation energy, E, of the main crystallization process varies between 2.7 and 4.7 eV at.-1. The E values obtained remains similar with the storage time. Small contamination from the milling tools was found. Furthermore, powdered alloys are more sensible to oxidation processes than as quenched ribbons ​