Microstructure and magnetic properties of Ni50 Mn37 Sn13 Heusler alloy ribbons
dc.contributor.author
dc.date.accessioned
2011-02-07T13:51:10Z
dc.date.available
2010-12-14T10:36:29Z
2011-02-07T13:51:10Z
dc.date.issued
2008
dc.identifier.citation
Santos, J.D., Sánchez, T., Álvarez, P., Sánchez, M.L., Llamazares, J.L.S., Hernándo, B., Escoda, Ll., Suñol, J.J. i Varga, R. (2008). Microstructure and magnetic properties of Ni50 Mn37 Sn13 Heusler alloy ribbons. Journal of Applied Physics, 103 (7), 07B326. Recuperat 7 febrer 2011, a http://link.aip.org/link/JAPIAU/v103/i7/p07B326/s1
dc.identifier.issn
0021-8979
dc.identifier.uri
dc.description.abstract
The Heusler alloy Ni50 Mn37 Sn13 was successfully produced as ribbon flakes of thickness around 7-10 μm melt spinning. Fracture cross section micrographs in the ribbon show the formation of a microcrystalline columnarlike microstructure, with their longer axes perpendicular to the ribbon plane. Phase transition temperatures of the martensite-austenite transformation were found to be MS =218 K, Mf =207 K, AS =224 K, and Af =232 K; the thermal hysteresis of the transformation is 15 K. Ferromagnetic L 21 bcc austenite phase shows a Curie point of 313 K, with cell parameter a=0.5971 (5) nm at 298 K, transforming into a modulated 7M orthorhombic martensite with a=0.6121 (7) nm, b=0.6058 (8) nm, and c=0.5660 (2) nm, at 150 K
dc.format.mimetype
application/pdf
dc.language.iso
eng
dc.publisher
American Institute of Physics
dc.relation.isformatof
Reproducció digital del document publicat a: http://dx.doi.org/10.1063/1.2832330
dc.relation.ispartof
© Journal of Applied Physics, 2008, vol. 103, núm. 7
dc.relation.ispartofseries
Articles publicats (D-F)
dc.rights
Tots els drets reservats
dc.subject
dc.title
Microstructure and magnetic properties of Ni50 Mn37 Sn13 Heusler alloy ribbons
dc.type
info:eu-repo/semantics/article
dc.rights.accessRights
info:eu-repo/semantics/openAccess
dc.identifier.doi
dc.identifier.idgrec
010562
dc.identifier.eissn
1089-7550