Evaluación de las propiedades de materiales compuestos fabricados a partir de fibras semiquímicas de Leucaena collinsii y polipropileno

Abstract

This thesis studies the effect produced by the reinforcement of polypropylene with a semichemical fibre of Leucaena collinsii in the mechanical, thermal and water uptake properties.

Samples with different reinforcement content are obtained and stabilized in a climatic chamber for 48 hours before being tested to tensile, flexural and the termal properties are studied by TGA, DSC, TMA, DMA and thermal conductivity test. Finally, the water uptake maximum capacity was determined.

The addition of increasing quantities of reinforcement increases the maximum resistance and stiffne of the material, but a diminution of the deformation capacity was observed. None of the thermal transitions were affected by the addition of reinforcement. However, the crystallinity increased when increasing the fiber content

La presente tesis estudia el efecto que produce reforzar una fibra semiquímica de Leucaena collinsii en las propiedades mecánicas, térmicas y de sorción de agua de materiales compuestos de polipropileno.

Se obtienen probetas de materiales compuestos con distinto contenido de refuerzo y se estabilizan en una cámara climática durante 48 horas antes de ser ensayadas a tracción, flexión e impacto, y se analiza la morfologia de la fractura mediante SEM. Posteriormente se estudian sus propiedades térmicas mediante TGA, DSC, TMA, DMA y el análisis de la conductividad térmica de los materialses. Finalmente, se determinará la capacidad para absorber agua de estos compuestos.

La adición de cantidades crecientes de refuerzo provoca un aumento de la resistencia máxima y de la rigidez del material, pero una disminución de su capacidad de deformación. Las temperaturas de transición no se ven afectadas pero sí su cristalinidad, aumentando al añadir contenidos superiores de refuerzo