Exchange bias behavior in Ni 50.0Mn 35.5 In 14.5 ribbons annealed at different temperatures

Full Text
Exchange-bias-behavior.pdf embargoed access
Request a copy
When filling the form you are requesting a copy of the article, that is deposited in the institutional repository (DUGiDocs), at the autor or main autor of the article. It will be the same author who decides to give a copy of the document to the person who requests it, if it considers it appropriate. In any case, the UdG Library doesn’t take part in this process because it is not authorized to provide restricted articles.
Heusler alloy Ni 50.0Mn 35.5In 14.5 ribbons were prepared by melt-spinning technique. Several short time annealings were carried out in order to enhance the exchange bias effect in this alloy ribbon. The magnetic transition temperature increases with the annealing, compared to the as-spun sample, however no significant differences in respective Curie temperatures were observed for austenite and martensite phases in such annealed samples. Exchange bias effect is observed at low temperatures for all samples and practically vanishes at 60 K for the as-spun sample, whereas for the annealed ribbons it vanishes at 100 K ​
​Tots els drets reservats